2061支临床废弃手用ProTaper锉的损伤分析

上海口腔医学 ›› 2013, Vol. 22 ›› Issue (5): 528-532.

2061支临床废弃手用ProTaper锉的损伤分析

顾永春^1,2，倪龙兴²

(1.南通大学附属吴江医院口腔科，江苏苏州 215200；2.第四军医大学口腔医学院牙体牙髓病科，陕西西安 710032)

收稿日期:2013-03-25 修回日期:2013-04-26 出版日期:2013-10-10 发布日期:2013-10-10
通讯作者: 顾永春，Tel：0512-63000715,E-mail：guyc7152@163.com
作者简介:顾永春(1971-)，男，博士，副主任医师

Defects in 2061 discarded ProTaper handfiles after clinical use

GU Yong-chun^1,2, Ni Long-xing²

1.Department of Stomatology, Affiliated Hospital of Wujiang, Nantong University. Suzhou 215200, Jiangsu Province; 2.Department of Endodontics, College of Stomatology, Fourth Military Medical University. Xi’an 710032, Shaanxi Province, China

Received:2013-03-25 Revised:2013-04-26 Online:2013-10-10 Published:2013-10-10

摘要/Abstract

摘要： 目的：探讨手用ProTaper锉的损伤、断裂机制。方法：从临床采集2061支废弃的手用ProTaper镍钛锉，体视显微镜下观察锉刃损伤及塑性变形状况，对断锉进行微距数码摄影，Image-Pro Plus软件测量分析断点的位置。采用SPSS 11.0 软件包对数据进行统计学分析。结果：166支锉锉刃发生塑性形变(8.2%)，塑性形变类型包括解旋、紧致螺旋、塑性弯曲变形； 581支锉发生器械分离，折断率为28.2%。F2锉组折断率最高(41.7%)，而SX锉组断点水平最高，距离锉尖平均距离为(4.4±1.1) mm。结论：ProTaper手用锉预备根管时，直径较细的成形锉以及靠近锉尖端以扭转折断为主，直径较大的修形锉以及远离锉尖段以旋转疲劳断裂为主。掌握ProTaper手用锉的损伤类型，对根管治疗中避免器械分离具有重要意义。

关键词: 器械分离, ProTaper锉, 疲劳失效

Abstract: PURPOSE: To explore the mechanism of failure of ProTaper NiTi handfiles during root canal preparation. METHODS: A total of 2061 discarded ProTaper handfiles were collected after clinical use. The files were studied under stero-microscope to determine the type of defect. The fractured files were photographed digitally and the pictures were analyzed by software Image-Pro Plus to measure the distance from the break point to the tip. The data were statistically analyzed by using SPSS 11.0 software package. RESULTS: Plastic deformation was observed in 166 files (8.2%), and the types of defects included unwinding, winding flutes, and plastic bending. Instrument separation occurred in 581 files (28.2%), and the fracture rate was the highest in the F2 file group (41.7%). The SX file group had the highest facture level, and the mean distance from the breakpoint to the file tip was (4.4±1.1) mm. CONCLUSIONS： For shaping files, especially at the apical level, the main cause of mental failure is overload of torque, whereas for finishing files, especially at the higher level, is cycle fatigue. Understanding the defect types of ProTaper handfiles is useful for avoiding file breakage during root canal therapy.

Key words: Instrument separation, ProTaper, Fatigue failure

中图分类号:

R781.05

顾永春, 倪龙兴. 2061支临床废弃手用ProTaper锉的损伤分析[J]. 上海口腔医学, 2013, 22(5): 528-532.

GU Yong-chun, Ni Long-xing. Defects in 2061 discarded ProTaper handfiles after clinical use[J]. Shanghai Journal of Stomatology, 2013, 22(5): 528-532.

参考文献

[1] 彭彬, 沈雅. 镍钛合金根管器械折断的临床特点及预防[J]. 继续医学教育, 2006, 20(22): 17-20.
[2] 顾永春, 周培刚, 丁月峰. 手用ProTaper对弯曲根管的成形能力的评价的研究[J]. 口腔医学, 2007, 27(10): 535-538.
[3] 徐琼, 范兵, 樊明文, 等. ProTaper预备弯曲根管的临床评价[J]. 中华口腔医学杂志, 2004, 39(2): 50-52.
[4] 罗红霞, 黄定明. ProTaper根管预备器械的研究现状[J]. 国外医学?口腔医学分册, 2005, 32(1): 61-63.
[5] Shen Y, Bian Z, Cheung GS, et al. Analysis of defects in ProTaper hand-operated instruments after clinical use[J]. J Endod, 2007, 33(3): 287-290.
[6] Peng B, Shen Y, Cheung GS, et al. Defects in ProTaper S1 instruments after clinical use: longitudinal examination[J]. Int Endod J, 2005, 38(8): 550-557.
[7] Cheung GS, Peng B, Bian Z, et al. Defects in ProTaper Sl instruments after clinical use: fractographic examination[J]. Int Endod J, 2005, 38(11): 802-809.
[8] Shen Y, Peng B, Cheung GS. Factors associated with the removal the fractured NiTi instruments from root canal systems[J]. Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 2004, 98(5): 605-610.
[9] 袁理, 岳林, 王嘉德. Hero642 镍钛锉断裂损伤德形态研究[J]. 实用口腔医学杂志, 2006, 22(5): 604-607.
[10] Iqbal MK, Kohli MR, Kim JS. A retrospective clinical study of incidence of root canal instrument separation in an endodontics graduate program: a PennEndo database study[J]. J Endod, 2006, 32(11): 1048-1052.
[11] Sattapan B, Nervo GJ, Palamara JE, et al. Defects in rotary nickel-titanium files after clinical use[J]. J Endod, 2000, 26(3): 161-165.
[12] 顾永春. 根管器械弯曲、扭转负载下的力学分析[J]. 牙体牙髓牙周病学杂志, 2008, 18(10): 568-580.
[13] 程靳, 赵树山. 断裂力学[M]. 北京: 科学出版社, 2006: 145-157.
[14] Ullmann CJ, Peters OA. Effect of cyclic fatigue on static fracture loads in ProTaper nickel-titanium rotary instruments[J]. J Endod, 2005, 31(3): 183-186.