采用几种参数制作的激光熔积钴铬合金表面EDS能谱分析

钱亮1,曾丽1,魏斌1,宮耀2   

  1. 1.上海交通大学医学院附属第九人民医院·口腔医学院 口腔特需门诊,上海市口腔医学重点实验室,上海 200011;
    2. 上海交通大学医学院附属第九人民医院·口腔医学院 口腔正畸科,上海市口腔医学重点实验室,上海 200011
  • 收稿日期:2015-03-13 出版日期:2015-06-20 发布日期:2015-07-24
  • 通讯作者: 宫耀,E-mail:gongyao0328@hotmail.com
  • 作者简介:钱亮（1991-）,女,在读硕士研究生,E-mail:369078249@qq.com
  • 基金资助:
    科技部“973”项目（2012CB910401）; 上海市科学技术委员会资助项目（12441903001,13140902701）

Energy dispersive spectrum analysis of surface compositions of selective laser melting cobalt-chromium alloy fabricated by different processing parameters

QIAN Liang1,ZENG Li1,WEI Bin1,GONG Yao2   

  1. 1.Department of Stomatology Special Consultation Clinic, Shanghai Ninth People’s Hospital, College of Stomatology, Shanghai Jiao Tong University School of Medicine; Shanghai Key Laboratory of Stomatology. Shanghai 200011,China;
    2. Department of Orthodontics, Shanghai Ninth People’s Hospital, College of Stomatology, Shanghai Jiao Tong University School of Medicine; Shanghai Key Laboratory of Stomatology. Shanghai 200011,China
  • Received:2015-03-13 Online:2015-06-20 Published:2015-07-24
  • Supported by:
    "973" Program (2012CB910401) and Research Fund of Science and Technology Committee of Shanghai Municipality (12441903001 and 13140902701).

RichHTML

1

PDF (PC)

306

被引次数

1

摘要： 目的:采用几种工艺参数制作激光熔积钴铬合金试样,研究其表面EDS能谱的变化。方法:根据激光功率、扫描速度、送粉速率数值的不同（激光功率2500~3000 W、扫描速度5~15 mm/s、送粉速度3~6 r/min）,采用正交实验设计9组试验组,利用自主研发的Co-Cr合金金属粉末,分别通过Rofin DL 035Q激光熔附系统制作3个圆柱形SLM钴铬合金试件（直径10 mm,厚度3 mm）,对9组试件分别行EDS能谱分析,测定试件表面成分及含量。结果:在设定的工艺参数下,9组试件的EDS能谱分析结果(Co：62.98%~67.13%,Cr：25.56% ~28.50%,Si：0.49%~1.23%)均与临床常用钴铬合金组成相似。结论:根据表面EDS能谱分析结果,在本实验采用的各种参数下,制成的SLM钴铬合金试件的表面成分稳定、可控。

关键词: 选择性激光熔积, 钴铬合金, 表面成分, EDS能谱分析

Abstract: PURPOSE: To fabricate selective laser melting cobalt-chromium alloy samples by different processing parameters, and to analyze the changes of energy dispersive spectrum(EDS) on their surface. METHODS: Nine groups were set up by orthogonal experimental design according to different laser powers,scanning speeds and powder feeding rates(laser power:2500~3000 W, scanning speed: 5~15 mm/s, powder feeding rate: 3~6 r/min). Three cylinder specimens(10 mm in diameter and 3 mm in thickness)were fabricated in each group through Rofin DL 035Q laser cladding system using cobalt-chromium alloy powders which were developed independently by our group.Their surface compositions were then measured by EDS analysis. RESULTS: Results of EDS analysis of the 9 groups fabricated by different processing parameters(Co：62.98%-67.13%,Cr：25.56%-28.50%,Si：0.49%-1.23%) were obtained. They were similar to the compositions of cobalt-chromium alloy used in dental practice. CONCLUSIONS: According to EDS results, the surface compositions of the selective laser melting cobalt-chromium alloy samples are stable and controllable, which help us gain a preliminary sight into the range of SLM processing parameters.

Key words: Selective laser melting, Cobalt-chromium alloy, Surface composition, Energy dispersive spectrum analysis